옵티멈윈도우필름::글로벌 윈도우 틴터그룹

		IR 06	IR 14	IR 30
1	THICKNESS	2.0 mil	2.0 mil	2.0 mil
2	PLY	2 Ply	2 Ply	2 Ply
3	% VISBILE LIGHT TRANSMISSION (VLT%)	6	14	30
4	% VISBILE LIGHT TRANSMISSION TOLERANCE	6 ± 1.5	14 ± 2.5	30 ± 3.0
5	% VISIBLE LIGHT REFLECTION	6	6	6
6	% SOLAR ENERGY TRANSMISSION	5	9	16
7	% SOLAR ENERGY REFLECTED	6	6	6
8	% SOLAR ENERGY ABSORBED	89	85	78
9	% U. V. TRANSMITTANCE	< 1	< 1	< 1
10	% TOTAL SOLAR ENERGY REJECTED (TSER)	70	67	62
11	SHADING COEFF	0.34	0.37	0.43
12	% GLARE REDUCTION	93	85	67
13	NIR BLOCKING AT 1025NM	96 ± 3.0	96 ± 3.0	96 ± 3.0
NOTE
The performance data reported on this page was tested at DSET Lab & MATRIX Lab,USA using ASHRAE,ASTM & AIMCOL Standards. All the values as applied on 1/8"(3mm) glass .Tests are representative of actual production sample & may vary from batch to batch. Tolerance provided for Visible light transmittance, other performance parameters will change accordingly

		XT 05	XT 13	XT 42
1	THICKNESS	1.5 mil	1.5 mil	1.5 mil
2	PLY	2 Ply	2 Ply	2 Ply
3	% VISBILE LIGHT TRANSMISSION (VLT%)	5	13	42
4	% VISBILE LIGHT TRANSMISSION TOLERANCE	5.5 ± 1.5	13 ± 2.0	42 ± 3.0
5	% VISIBLE LIGHT REFLECTION	6	8	9
6	% SOLAR ENERGY TRANSMISSION	5	10	21
7	% SOLAR ENERGY REFLECTED	6	8	8
8	% SOLAR ENERGY ABSORBED	89	82	71
9	% U. V. TRANSMITTANCE	< 1	< 1	< 1
10	% TOTAL SOLAR ENERGY REJECTED (TSER)	70	67	59
11	SHADING COEFF	0.34	0.38	0.47
12	% GLARE REDUCTION	94	86	54
13	NIR BLOCKING AT 1025NM	90 ± 3.0	90 ± 3.0	90 ± 3.0
NOTE
The performance data reported on this page was tested at DSET Lab & MATRIX Lab,USA using ASHRAE,ASTM & AIMCOL Standards. All the values as applied on 1/8"(3mm) glass .Tests are representative of actual production sample & may vary from batch to batch. Tolerance provided for Visible light transmittance, other performance parameters will change accordingly

		CP 04	CP 18	CP 32	CP 46
1	THICKNESS	2.0 mil	2.0 mil	2.0 mil	2.0 mil
2	PLY	2 Ply	2 Ply	2 Ply	2 Ply
3	% VISBILE LIGHT TRANSMISSION (VLT%)	4	18	32	46
4	% VISBILE LIGHT TRANSMISSION TOLERANCE	4.5 ± 1.5	19 ± 3.0	31 ± 3.0	46 ± 3.0
5	% VISIBLE LIGHT REFLECTION	6	6	7	7
6	% SOLAR ENERGY TRANSMISSION	11	16	23	30
7	% SOLAR ENERGY REFLECTED	6	6	6	6
8	% SOLAR ENERGY ABSORBED	83	78	71	64
9	% U. V. TRANSMITTANCE	< 1	< 1	< 1	< 1
10	% TOTAL SOLAR ENERGY REJECTED (TSER)	66	62	57	52
11	SHADING COEFF	0.39	0.4	0.49	0.55
12	% GLARE REDUCTION	96	80	65	49
13	NIR BLOCKING AT 1025NM	78 ± 3.0	78 ± 3.0	78 ± 3.0	78 ± 3.0
NOTE
The performance data reported on this page was tested at DSET Lab & MATRIX Lab,USA using ASHRAE,ASTM & AIMCOL Standards. All the values as applied on 1/8"(3mm) glass .Tests are representative of actual production sample & may vary from batch to batch. Tolerance provided for Visible light transmittance, other performance parameters will change accordingly

		HP 04	HP 14	HP 39
1	THICKNESS	1.5 mil	1.5 mil	1.5 mil
2	PLY	2 Ply	2 Ply	2 Ply
3	% VISBILE LIGHT TRANSMISSION (VLT%)	4	14	39
4	% VISBILE LIGHT TRANSMISSION TOLERANCE	4 ± 1.5	14 ± 2.0	39 ± 3.0
5	% VISIBLE LIGHT REFLECTION	5	7	8
6	% SOLAR ENERGY TRANSMISSION	21	23	45
7	% SOLAR ENERGY REFLECTED	12	13	7
8	% SOLAR ENERGY ABSORBED	67	64	48
9	% U. V. TRANSMITTANCE	< 1	< 1	< 1
10	% TOTAL SOLAR ENERGY REJECTED (TSER)	61	59	41
11	U- VALUE	1.03	1.11	1.12
12	SHADING COEFF	0.46	0.48	0.68
13	EMMI-SIVITY	0.78	0.76	0.84
14	% GLARE REDUCTION	96	85	57
NOTE
The performance data reported on this page was tested at DSET Lab & MATRIX Lab,USA using ASHRAE,ASTM & AIMCOL Standards. All the values as applied on 1/8"(3mm) glass .Tests are representative of actual production sample & may vary from batch to batch. Tolerance provided for Visible light transmittance, other performance parameters will change accordingly